Copper Alloys C11000 is stocked by 91 North American distributors and produced by 48 large mills. Distributors will offer small quantity buys while mills will generally only sell large quantities, with delivery times anywhere from 10 to 50 weeks depending on size and form required
This material is stocked primarily in Flat Rolled Products by 75 distributors but is also available to a lesser extent in Bar Products, Wire Products, Tubular Products, Shapes, and Forging Products.
For distributor (small quantity) availability click here
For mill (large volume) production click here
To view all click here
Specifications
The following specifications cover Copper Alloys C11000
- ASME SB133
- ASTM B1
- ASTM B101
- ASTM B116
- ASTM B124
- ASTM B133
- ASTM B152
- ASTM B172
- ASTM B173
- ASTM B174
- ASTM B187
- ASTM B188
- ASTM B189
- ASTM B2
- ASTM B224
- ASTM B226
- ASTM B228
- ASTM B229
- ASTM B246
- ASTM B272
- ASTM B283
- ASTM B286
- ASTM B298
- ASTM B3
- ASTM B33
- ASTM B355
- ASTM B370
- ASTM B447
- ASTM B451
- ASTM B47
- ASTM B470
- ASTM B48
- ASTM B49
- ASTM B496
- ASTM B506
- ASTM B556
- ASTM B638
- ASTM B694
- ASTM B738
- ASTM B8
- ASTM F467
- ASTM F468
- MIL B-20292
- MIL C-12168
- MIL W-6712
- QQ B575
- SAE J461
- SAE J463
- UNS C11000
Property Results
Related Metals:
- Copper Alloy 110
- ETP Copper, C110
Chemistry Data : [top]
|
Principal Design Features
|
|
Copper, ETP, Electrolytic Tough Pitch. Has conductivity 101% IACS. Ductile, anneal resistant.
|
|
|
Applications
|
|
C11000 is mainly used for plumbing fittings and some electrical components not requiring extensive machining.
|
|
|
Machinability
|
|
The machinability rating of this alloy is 20. (Where Alloy 360 FC Brass is 100).
|
|
|
Welding
|
|
Soldering is rated as "excellent", brazing is rated as "good", oxyacetylene welding is "not recommended", gas shielded arc welding is rated as "fair", coated metal arc welding is "not recommended", spot welding is "not recommended", seam welding is "not recommended" and butt welding is rated as "good".
|
|
|
Forging
|
|
The hot forgeability rating of this alloy is 65. (Forging brass = 100). The recommended hot working temperature for this alloy is between 1400 and 1600 F.
|
|
|
Hot Working
|
|
This alloy's capacity for being hot formed is rated as "excellent".
|
|
|
Cold Working
|
|
The capacity for cold working this alloy is rated as "excellent".
|
|
|
Annealing
|
|
The annealing temperature for this alloy is between 700 and 1200 F.
|
|
Physical Data : [top]
|
|
|
Density (lb / cu. in.)
|
0.323
|
|
Electrical Resistivity (microhm-cm (at 68 Deg F))
|
10.3
|
|
Melting Point (Deg F)
|
1949
|
|
Mean Coeff Thermal Expansion
|
9.4
|
|
Modulus of Elasticity Tension
|
17000
|
Mechanical Data : [top]
|
MSO currently has no data available for this grade.
|
Videos :
|
MSO currently has no videos available for this grade.
|
Disclaimer
This information is provided "as is" and Metal Suppliers Online, Inc. makes no warranty of any kind with respect to the subject matter or accuracy of the information contained herein. Metal Suppliers Online, Inc. specifically disclaims all warranties, expressed, implied or otherwise, including without limitation, all warranties of merchantability and fitness for a particular purpose.
In no event shall Metal Suppliers Online, Inc. be liable for any special, incidental, indirect or consequential damages of any kind or any damages whatsoever resulting from loss of use, data, profits, whether or not advised of the possibility of damage, and on any theory of liability, arising out of or in connection with the use of the information contained herein.
This publication may include technical inaccuracies or typographical errors. Changes may be periodically made to the information herein.