Copper Alloys C63000 is stocked by 24 North American distributors and produced by 4 large mills. Distributors will offer small quantity buys while mills will generally only sell large quantities, with delivery times anywhere from 10 to 50 weeks depending on size and form required
This material is stocked primarily in Bar Products by 18 distributors but is also available to a lesser extent in Casting Products, Tubular Products, Flat Rolled Products, Forging Products, Shapes, and Wire Products.
For distributor (small quantity) availability click here
For mill (large volume) production click here
To view all click here
Specifications
The following specifications cover Copper Alloys C63000
- ASME SB150
- ASME SB171
- ASTM B124
- ASTM B150
- ASTM B171
- ASTM B283
- ASTM F467
- ASTM F468
- MIL B-16166
- QQ C450
- SAE J461
- SAE J463
- UNS C63000
Property Results
Related Metals:
Chemistry Data : [top]
Aluminum
|
|
9 - 11 |
Copper
|
|
Balance |
Iron
|
|
2 - 4 |
Manganese
|
|
1.5 max |
Nickel
|
|
Including Co |
Remainder Each
|
|
Cu, including Ag |
Remainder Total
|
|
Cu + sum of named elements 99.5 min |
Silicon
|
|
0.25 max |
Tin
|
|
0.2 max |
Zinc
|
|
0.3 max |
|
Principal Design Features
|
|
Bronzes (Copper-Aluminum), 10%. C63000 has typical tensile strength of 118 ksi (814 MPa). Excellent corrosion resistance.
|
|
|
Applications
|
|
Applications include valve and pump components for industrial process streams, as well as for marine equipment, high strength fasteners and pole line hardware.
|
|
|
Machinability
|
|
The machinability rating of this alloy is 30. (Where Alloy 360 FC Brass is 100).
|
|
|
Welding
|
|
Soldering of this alloy is "not recommended", brazing is rated as "fair", oxyacetylene welding is "not recommended", gas shielded arc welding is rated as "good", coated metal arc welding is rated as "good", spot welding is rated as "good", seam welding is rated as "good", and butt welding is rated as "good".
|
|
|
Forging
|
|
The hot forgeability rating of this alloy is 75. (Forging Brass=100). The recommended hot working temperature for this alloy is between 1450 and 1700 F.
|
|
|
Hot Working
|
|
This alloy's capacity for being hot formed is rated as "good".
|
|
|
Cold Working
|
|
The capacity for cold working this alloy is rated as "poor".
|
|
|
Annealing
|
|
The annealing temperature for this alloy is between 1100 and 1300 F.
|
|
Physical Data : [top]
|
|
|
Density (lb / cu. in.)
|
0.274
|
|
Electrical Resistivity (microhm-cm (at 68 Deg F))
|
116
|
|
Melting Point (Deg F)
|
1895
|
|
Modulus of Elasticity Tension
|
17500
|
Mechanical Data : [top]
|
MSO currently has no data available for this grade.
|
Videos :
|
MSO currently has no videos available for this grade.
|
Disclaimer
This information is provided "as is" and Metal Suppliers Online, Inc. makes no warranty of any kind with respect to the subject matter or accuracy of the information contained herein. Metal Suppliers Online, Inc. specifically disclaims all warranties, expressed, implied or otherwise, including without limitation, all warranties of merchantability and fitness for a particular purpose.
In no event shall Metal Suppliers Online, Inc. be liable for any special, incidental, indirect or consequential damages of any kind or any damages whatsoever resulting from loss of use, data, profits, whether or not advised of the possibility of damage, and on any theory of liability, arising out of or in connection with the use of the information contained herein.
This publication may include technical inaccuracies or typographical errors. Changes may be periodically made to the information herein.